Bambu Lab PAHT-CF
Bambu Lab PAHT-CF is a carbon fiber reinforced high-temperature nylon filament.
Bambu PAHT-CF is a composite material made from PA12 and carbon fiber. Bambu PAHT-CF combines the advantages of PA12's low water absorption and high-performance carbon fibers, offering excellent mechanical and thermal properties that remain stable even when the prints get wet. Increased Z-layer adhesion and flexibility make it ideal for producing technical parts such as functional prototypes, machining fixtures, injection molds, jigs, and small-batch production parts.
Low Water Absorption
With a 50% lower water absorption rate compared to regular PA-CF,
Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability, even when exposed to high humidity.
Performance from Dry to Wet
Exceptional Z-Bonding
Bambu PAHT-CF exhibits much higher Z-layer adhesion compared to regular PA-CF,
allowing it to withstand strong impacts or loads without breaking or deforming.
Z-Layer Performance
Regular PA-CF | PAHT-CF | Improved % | |
Flexural Strength – Z/MPa | 48 | 61 | 27 % |
Flexural Modulus – Z/MPa | 1470 | 1820 | 24 % |
Impact Strength – Z/(kJ/m²) | 5.7 | 13.3 | 133 % |
*Both PA-CF and PAHT-CF need to be dried at 80°C for 12 hours before printing.
High Tensile Strength
Bambu PAHT-CF is designed to meet the requirements of various industries
and technical applications where high strength and durability are required.
Designed for High Temperature Resistance
The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45 MPa)*, making it suitable for applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.
*The long-term temperature resistance depends on the structure and usage scenario of the model itself.
Accessory Compatibility
Recommended | Not Recommended | |
Build Plate | High Temperature Plate - Engineering Plate | Cooling Plate |
Hotend | Hotend with hardened steel nozzle (0.6 mm, 0.4 mm, 0.8 mm)* | Hotend with stainless steel nozzle (all sizes) Hotend with hardened steel nozzle (0.2 mm) |
Glue | Glue Stick | Liquid Glue |
*As nozzle size increases, the likelihood of clogging decreases, but print quality also diminishes. Therefore, a 0.6 mm hardened steel nozzle is recommended to prevent clogging while maintaining optimal print quality.
Parameter Comparison
For more information on comparing different filaments, see the Bambu Filament Guide >>
PET-CF | PAHT-CF | |
Composition | PET, carbon fiber | PA 12 and other long-chain PA, carbon fiber |
Hotend Compatibility | Hardened steel 0.6 (recommended), 0.4, 0.8 mm | |
Build Plate Compatibility | Engineering Plate, High Temperature Plate, Textured PEI Plate | |
Glue | Glue Stick/Liquid Glue | Glue Stick |
AMS Compatibility | NO | YES |
Printing Speed | < 100 mm/s | < 100 mm/s |
Toughness (Impact Strength – XY) | 36.0 kJ/m² | 57.5 kJ/m² |
Strength (Flexural Strength – XY) | 131 MPa | 125 MPa |
Stiffness (Flexural Modulus – XY) | 5320 MPa | 4230 MPa |
Layer Adhesion (Impact Strength – Z) | 4.5 kJ/m² | 13.3 kJ/m² |
Heat Resistance (HDT, 0.45 MPa) | 205 °C | 194 °C |
Saturated Water Absorption Rate / % (25 °C, 55% relative humidity) | 0.37 | 0.88 |
Recommended Printing Settings
Recommended Printing Settings | |
Drying Settings (Oven) | 80 °C, 8 - 12 h |
Printing and Maintaining Container Humidity | < 10% |
Printing Speed | < 100 mm/s |
Printing Temperature | 300 - 320 °C |
Bed Temperature | 100 - 120 °C |
Bed Adhesion | Glue Stick |
Fan Speed | Off / 0% |
Minimum Nozzle Diameter | 0.4 mm (0.6 mm recommended) |
Technical Data
Material Properties | |
Base Material | PA12 |
Reinforcing Material | Carbon Fiber |
Color | Black |
Diameter | 1.75 mm |
Net Weight | 500 g |
Roundness | ± 0.04 mm |
Filament Length Tolerance | ± 0.02 mm |
Art: | Filament |
Property: | Faserverstärkt |
Material: | PA CF |
Color: | black |
Radius: | 1,75 mm |
Weight: | 500 g, 1000 g |